Polymaker PolySmooth Transparent 2.85mm 750g

PolySmooth™ is a unique, easy-to-print filament designed for healthier and easier post processing. The magic of this process occurs because the filament is soluble in alcohol. Thus, surfaces can be smoothed with alcohol achieving a layer free model.

Polymaker recommends that this material be used with the PolyBox™ to keep it at dry conditions (relative humidity of 15% or less) at all times to maintain the best printing results.

Features

• Easy Post Processing - As PolySmooth is soluble in alcohol, Isopropyl alchol can be utilized to acheive a layer free model
• Balanced Mechanical Properties - PolySmooth™ features well balanced mechanical properties, outperforming ABS and PLA on many attributes, making it an ideal material for everyday 3D printing.
• Easy-to-print - PolySmooth™ is compatible with most 3D printers, printing under similar conditions to regular PLA. No heated bed required but can be used for best results (up to 70°C). Polymaker have also optimized PolySmooth™ to allow easy removal of support.
• Uncompromised Quality - Polymakers leading quality control process and rigorous in-house testing ensure reliable printing and consistency across spools and batches.

Specifications

Print Settings

• Nozzle Temperature: 190˚C – 220˚C
• Printing Speed: 40mm/s – 60mm/s
• Bed Temperature: 25˚C – 70˚C
• Bed Surface: Glass with glue, Blue Tape
• Cooling Fan: ON

Note: Based on 0.4 mm nozzle and Simplify 3D v.3.1. Printing conditions may vary with different printers and nozzle diameters.

Mechanical Properties

• Young’s Modulus: 2047 ± 111 Mpa
• Tensile Strength: 39.8 ± 0.7 Mpa
• Bending Strength: 64.9 ± 1.2 Mpa
• Impact Strength: 9.2 ± 1.2 kJ/m2

Thermal Properties

• Glass Transition Temperature: 70˚C
• Vicat Softening Temperature: 70˚C
• Melting Temperature: N/A

Notes

• Drying Settings: 80˚C for 8h
• Recommended Support Materials: PolyDissolve™ S1
• It is highly recommended to use the PolyBox™ when printing with PolySmooth™ and to store it in the resealable bag.